High Performance Uns No6455/Ns335 /W. Nr. 2.4610 Nimo16cr16ti Hastelloy C-4 for Hot Sale

• Customization: Available
• Product Type: Wire
• Carbon Content: Low Carbon
• Model NO.: Hastelloy C-4
• Condition: Bright, Annealed
• Price: Low
• Quality: High
• Surface: Smooth
• Transport Package: in Spool, Carton, Wooden Case
• Trademark: Ualloy
• Origin: China
• HS Code: 75052200
• Production Capacity: 500 Tons/Year
• Package Size: 50.00cm * 40.00cm * 30.00cm
• Package Gross Weight: 50.000kg

Product Description

Hangzhou Ualloy Material Co.,Ltd is one of the best corrosion resistance alloy Hastelloy C - 4manufacturers and suppliers in China, welcome to buy discount and low price corrosion resistance alloy Hastelloy C - 4 from us, and also welcome to check the price and quotation with our factory.

Production Description

Hastelloy C - 4 (UNS NO6455)

Features and application field overview:

The alloy is an austenitic low carbon nickel-molybdenum-chromium alloy. The main difference between Nicrofer 6616 hMo and other alloys of similar chemical composition developed earlier is the low carbon, silicon, iron and tungsten content. Such chemical composition makes it exhibit excellent stability at 650-1040ºC, and improves its resistance to intergranular corrosion. Under appropriate manufacturing conditions, it can avoid the edge line corrosion sensitivity and weld heat affected zone corrosion. Alloys are used in flue gas desulfurization systems, pickling and acid regeneration plants, production of acetic acid and agricultural chemicals, production of titanium dioxide (chlorine), electroplating, etc.

Similar brand:

NS335 (China) w.nr.2.4610 NiMo16Cr16Ti (Germany) 

Chemical composition

 

Alloy brand	%	Ni	Cr	Fe	Mo	Co	C	Mn	S	Si	Ti
Hastelloy C-4	Min.	Bal.	14.5		14.0
	Max.		17.5	3.0	17.0	2.0	0.009	1.0	0.01	0.05	0.7

Physical properties:

Density g/cm3	Melting ºC	Thermal conductivity λ/(W/m•ºC)	Specific heat capacity  J/kg•ºC	Modulus of elasticit GPa	Resistivity μΩ•m	Coefficient of linear expansion  a/10-6ºC-1
8.6	1335 1380	10.1(100ºC)	408		1.24	10.9(20~100ºC)

Mechanical properties :(minimum value of mechanical properties at 20ºC)

Heat treatment method	tensile strength b/MPa	yield strength p0.2/MPa	elongationσ5 /%	Hardness    HBS
Solution treatment	690	275	40

 

Production execution standard:

	bar	forging	plate (strip)	wire	pipe
USA association  for materials    and testing	ASTM B574	ASTM B336	ASTM B575		ASTM B622 ASTM B619 ASTM B626
USA technical specification for aerospace materials
USA society of mechanical engineers	ASME SB335	ASME SB335	ASME SB333		ASTM SB622 ASTM SB619 ASTM SB626

 

Metallographic structure:

The alloy is surface centered cubic lattice structure, and its chemical composition guarantees the metallographic stability and resistance to sensitization.

 

Performance and requirements:

1. Do not contact sulfur, phosphorus, lead and other low-melting metals in the process of heat treatment, otherwise the alloy will become brittle. Please pay attention to remove dirt such as marker paint, temperature indicator paint, colored crayons, lubricating oil, fuel and so on. The lower the sulfur content in the fuel, the better. The sulfur content in natural gas should be less than 0.1%, and the sulfur content in heavy oil should be less than 0.5%. Electric furnace heating is a better choice, because the furnace can accurately control the temperature, clean furnace gas. If the gas furnace gas is pure enough, you can choose.

2. The hot processing temperature of the alloy ranges from 1080ºC to 900ºC, and the cooling method is water cooling or other rapid cooling method. In order to ensure the best anticorrosion performance, solid solution heat treatment should be carried out after hot working.