Fecral 1cr15al5 Resistance Heating Alloy Ribbon

• Customization: Available
• Product Type: Strip
• Material: Fecral
• Model NO.: 1cr15al5
• Carbon Content: Low Carbon
• Status: Bright,Oxidized,Acid White
• Resistivity: 1.28
• Hb: 200-260
• Thickness: 0.6-1.5mm
• Transport Package: Wooden Case, Wooden Pallet
• Specification: ISO9001, ISO14001
• Trademark: UALLOY
• Origin: China
• HS Code: 72209000
• Production Capacity: 500tons/Year

Product Description

Fecral 1cr15al5   Resistance Heating Alloy Ribbon 
1. Description
With the characteristics of high resistance, low coefficient of electric resistance, High operating temperature, good corrosion resistance under high temperature.
It is mainly used in electric locomotive, diesel locomotive, metro vehicle and high Speed moving car etc brake system brake resistor, electric ceramic cooktop, industrial furnace.

2. Specification
1). Locomotive resistance strip:
Thickness: 0.6mm-1.5mm
Width: 60mm-90mm

2). Electric ceramic cooktop resistance strip:
Thickness: 0.04mm-1.0mm
Width: 5mm-12mm
Thickness&Width: (0.04mm-1.0mm)× 12mm(above)

3). Low resistance ribbon:
Thickness&Width: (0.2mm-1.5mm)*5mm

4). Industrial furnace ribbon:
Thickness: 1.5mm-3.0mm
Width: 10mm-30mm

3. Features
Stable performance; Anti-oxidation; Corrosion resistance; High temperature stability; Excellent coil-forming ability; Uniform and beautiful surface condition without spots.

4. Packing detail
Spool, coil, wooden case(as per client's requiryment)

5. Products and services
1). Pass: ISO9001 certification, and SO14001cetification;
2). Fine after-sale services;
3). Small order accepted;
4). Stable properties in high temperature;
5). Fast delivery;

C	P	S		Mn		Si	Cr	Ni	Al	Fe	Other
Max
0.12	0.025		0.025		0.70	Max 1.0	13.0~15.0	Max 0.60	4.5~6.0	Bal.	-

Mechanical Properties

Max Continuous Service Temp	980ºC
Resisivity at 20ºC	1.28 ohm mm2/m
Density	7.4 g/cm3
Thermal Conductivity	52.7 KJ/m@h@ºC
Coefficient of Thermal Expansion	15.4×10-6/ºC
Melting Point	1450ºC
Tensile Strength	637~784 Mpa
Elongation	Min 12%
Section Variation Shrink Rate	65~75%
Repeatedly Bend Frequency	Min 5 times
Continuous Service Time	-
Hardness	200-260HB
Micrographic Structure	Ferrite
Magnetic Property	Magnetic

Temperature Factor of Electrical Resistivity

20ºC	100ºC	200ºC	300ºC	400ºC	500ºC	600ºC	700ºC	800ºC	900ºC	1000ºC
1	1.005	1.014	1.028	1.044	1.064	1.090	1.120	1.132	1.142	1.150