Nickel Silver Copper-Nickel-Zinc Alloy Rod GB Bzn18-18 Bar

• Customization: Available
• Product Type: Rod
• Material: Cu,Ni,Zn
• Model NO.: C7521
• Status: Bright
• Density g/cm3: 8.73
• Electrical Conductivity %Iacs: 6
• Thermal Conductivity W/(M.K): 32
• Modulus of Elasticity Gpa: 125
• Specific Heat J/(G.K): 0.34
• Cold-Workability: Excellent
• Machinability: Suitable
• Electric Plating Property: Excellent
• Hot DIP Tin Plating Property: Excellent
• Transport Package: in Coil, Carton, Wooden Case
• Specification: RoHS, SGS
• Trademark: Ualloy
• Origin: Zhejiang, China
• HS Code: 74082290
• Production Capacity: 500tons/Year

Product Description

1. Description
 
Copper-Nickel-Zinc alloy, also called nickel silver, German silver, new silver, nickel brass, albata, or electrum, is a copper alloy with nickel and often zinc. Nickel silver is named for its silvery appearance, but it contains no elemental silver unless plated.
 
Chemical Content(%)
 

Cu	Fe	Mn	Ni	Pb	Zn
61.0~67.0	< 0.25	< 0.5	16.5~19.5	< 0.1	Remainder

 
Mechanical Propertie

Condition	1/2 Hard	Hard	Annealed
Hardness	120 ~ 180 HV	Min. 150 HV	-
Tensile Strength	440 ~ 570 MPa	Min. 540 MPa	Min. 373 Mpa
Elongation	Min. 5%	Min. 5%	Min. 20%

 
Articles,Chemical composition

Articles				Chemical composition
GB	UNS	EN	JIS	Cu%	Ni%	Zn%
BZn18-18	C75200	CuNi18Zn20	C7521	62-66	16.5-19.5	Rem

 
Physical properties,fabrication properties

Physical properties					fabrication properties
density g/cm3	electrical conductivity %IACS	thermal conductivity W/(m.K)	modulus of elasticity GPa	specific heat J/(g.K)	cold-workability	machinability	electric plating property	hot dip tin plating property	weldability	corrosion
8.73	6	32	125	0.34	excellent	suitable	excellent	excellent	good	excellent

 
Mechanical properties

Mechanical properties
State	Hardness HV	Tension test			bending test
		Thickness mm	Tensile strength MPa	elongation %	thickness	angles	ID
0	-	0.1-5.0	≥375	≥20	≤1.6	180°	sticking closely
1/2H	120-180	0.1-5.0	440-570	≥5	≤1.6	180°	100% of thickness
					≤0.5		200% of thickness
H	150-210	0.1-0.15	540-640	-	≤1.6	180°	200% of thickness
		>0.15-5.0		≥3	≤0.5		400% of thickness
EH	≥185	0.1-5.0	≥610	-	-	-	-

 
Typical application
Shields,Liquid crystal oscillators,pressing parts


2. Specification
Rod/bar Diameter:3-600mm.
 
3. Packing detail 
 1). Coil (plastic spool) + compressed ply-wooden case + pallet 
 2). Coil (plastic spool) + carton + pallet  
 5. Products and services
 
4. Products and services
1). Pass: ISO9001 certification, and SO14001cetification;
2). Fine after-sale services;
3). Small order accepted;
4). Fast delivery;