Thermostat Bimetal Strip Imphy 108sp Tb 208/110 5j20110 (5J11)

• Customization: Available
• Type: Strip
• Standard: GB
• Model NO.: 5J20110
• Shape: Strip, Roll
• Surface Treatment: Polished
• Application: Utomatic Control Devices and Instrumentation
• Size: 0.05mm-3.0mm)T*(1mm-150mm)W
• Condition: Bright,Printed
• Property: Can Replace Kanthal 1200
• Brand: Ualloy
• Product Name: Thermostat Bimetal Strip Imphy 108sp Tb 208/110
• High Expansion Layer: Mn75ni15cu10
• Low Expansion Layer: Ni36
• Features: High Sensitivity
• Transport Package: Rolled, Then Packed Into Plywood Pallet or Case
• Trademark: UALLOY
• Origin: Hangzhou, China
• HS Code: 7226999090

Product Description

Thermostat bimetal strip IMPHY 108SP TB 208/110 5J20110(5J11)

(Common Name: Truflex P675R, Chace 7500,Telcon200, Kanthal 1200, IMPHY 108SP, DIN TB20110 , TB 208/110)

Bimetallic alloy,it is a kind of precision alloy bonding by two or more different expansion coefficients metal or alloy, whose shape changes at changing temperature.

One component layer in the thermal bimetal has a low coefficient of thermal expansion called passive layer; the other component layer has a high coefficient of thermal expansion called active layer. Sometimes, in order to get the  thermal bimetal with special properties, a third or fourth layer of metal or alloy may be added.
Generally, the passive layer is made of Invar alloy containing 34% to 50% of Ni; the active layer is made of brass, nickel, Fe-Ni-Cr, Fe-Ni-Mn and Mn-Ni-Cu alloy. Different types of thermal bimetal can be obtained by different combinations of active layer and passive layer materials, such as high temperature type, medium temperature type, low temperature type, high sensitivity type, corrosion resistant type, resistance type and quick action type.

Bimetallic 5J20110 holds very high thermal sensitivity and higher resistivity,but the modulus of elasticity and allowable stress is lower,it can improve the sensitivity of the instrument,decrease the size and increase the force.
 
Composition

Grade	5J20110
High expansion layer	Mn75Ni15Cu10
Low expansion layer	Ni36

 
Chemical composition(%)
 

Grade	C	Si	Mn	P	S	Ni	Cr	Cu	Fe
Ni36	≤0.05	≤0.3	≤0.6	≤0.02	≤0.02	35~37	-	-	Bal.

 

Grade	C	Si	Mn	P	S	Ni	Cr	Cu	Fe
Mn75Ni15Cu10	≤0.05	≤0.5	Bal.	≤0.02	≤0.02	14~16	-	9~11	≤0.8

Typical Physical properties

Density (g/cm3)	7.7
Electrical resistivity at 20ºC(ohm mm^2/m)	1.13 ±5%
Thermal conductivity, λ/ W/(m*ºC)	6
Elastic Modulus,  E/ Gpa	113~142
Bending K / 10^-6 ºC^-1(20~135ºC)	20.8
Temperature bending rate  F/(20~130ºC)10^-6ºC^-1	39.0%±5%
Allowable temperature (ºC)	-70~ 200
Linear temperature (ºC)	-20~ 150

Application: The material is mainly used as Non magnetic non matching ceramic sealing material in Gyro and other electric vacuum devices.

Style of supply

Alloys Name	Type	Dimension
5J20110	Strip	W= 1mm-150mm	T= 0.05mm-3.0mm