Soft Magnetic Alloy 1j85 Plate

Product Details
Customization: Available
Product Type: Plate
Material: Fe Ni
Shipping & Policy
Shipping Cost: Contact the supplier about freight and estimated delivery time.
Payment Methods:
visa mastercard discover JCB diners club american express T/T
PIX SPEI OXXO PSE OZOW
  Support payments in USD
Secure payments: Every payment you make at Made-in-china.com is protected by the platform.
Refund policy: Claim a refund if your order doesn't ship, is missing, or arrives with product issues.
Manufacturer/Factory & Trading Company

360° Virtual Tour

Secured Trading Service
Diamond Member Since 2012

Suppliers with verified business licenses

Audited Supplier

Audited by an independent third-party inspection agency

Number of Employees
15
Year of Establishment
2012-02-06
  • Soft Magnetic Alloy 1j85 Plate
  • Soft Magnetic Alloy 1j85 Plate
  • Soft Magnetic Alloy 1j85 Plate
  • Soft Magnetic Alloy 1j85 Plate
  • Soft Magnetic Alloy 1j85 Plate
  • Soft Magnetic Alloy 1j85 Plate
Find Similar Products

Basic Info.

Model NO.
1j85
Color
Bright
Sample
Accept
Packing
Wooden Packing
Transport Package
Coil, Woven Bag Pallet
Specification
customized
Trademark
ualloy
Origin
Hangzhou, China
Production Capacity
500tons/Year

Packaging & Delivery

Package Size
50.00cm * 50.00cm * 40.00cm
Package Gross Weight
50.000kg

Product Description

 

 

Soft Magnetic Alloy Strip/1j85

 

Common Name: Ni80Mo5, E11c, permalloy, 79HMA, PCS)

 

1J85 is a nickel-iron magnetic alloy, with about 80% nickel and 20% iron content. Invented in 1914 by physicist Gustav Elmen at Bell Telephone Laboratories, it is notable for its very high magnetic permeability, which makes it useful as a magnetic core material in electrical and electronic equipment, and also in magnetic shielding to block magnetic fields. Commercial permalloy alloys typically have relative permeability of around 100,000, compared to several thousand for ordinary steel.

In addition to high permeability, its other magnetic properties are low coercivity, near zero magnetostriction, and significant anisotropic magnetoresistance. The low magnetostriction is critical for industrial applications, allowing it to be used in thin films where variable stresses would otherwise cause a ruinously large variation in magnetic properties. Permalloy's electrical resistivity can vary as much as 5% depending on the strength and the direction of an applied magnetic field. Permalloys typically have the face centered cubic crystal structure with a lattice constant of approximately 0.355 nm in the vicinity of a nickel concentration of 80%. A disadvantage of permalloy is that it is not very ductile or workable, so applications requiring elaborate shapes, such as magnetic shields, are made of other high permeability alloys such as mu metal. Permalloy is used in transformer laminations and magnetic recording heads.

1J85 is widely used in radio-electronic industry, precision instruments, remote control and automatic control system.

 

Normal Composition%

Ni

79.0~81.0

Fe

Bal.

Mn

0.3~0.6

Si

0.15~0.3

Mo

4.8~5.2

Cu

≤0.2

       

C

≤0.03

P

≤0.02

S

≤0.02

   

Typical Mechanical Properties

Yield strength

Tensile Strength

Elongation

Mpa

Mpa

%

980

1030

3~50

 Typical Physical properties

Density (g/cm3)

8.75

Electrical resistivity at 20ºC(ohm*mm2/m)

0.56

Coefficient of linear expansion(20ºC~200ºC)X10-6/ºC 

10.9~11.2

Saturation magnetostriction coefficient λθ/ 10-6

0,5

Curie point   Tc/ ºC

400

 

 

The magnetic properties of alloys with high permeability in weak fields

1J85

Initial permeability

Maximum permeability

Coercivity

Saturation magnetic induction intensity

Сold-rolled strip/ sheet.

Thickness, mm

μ0.08/ (mH/m)

μm/ (mH/m)

Hc/ (A/m)

BS/ T

0.01 mm

20

87.5

4.8

 

 

 

 

 

 

 

 

 

 

0.75

0.1~0.19 mm

37.5

187.5

1.6

0.2~0.34 mm

50

225

1.2

0.35~1.0 mm

62.5

312.5

0.8

1.1~2.5 mm

50

187.5

1.2

2.6~3.0 mm

43.8

150

1.44

cold drawn wire

 

0.1 mm

8.7

37.6

6.4

Bar

 

8-100 mm

37.5

125

1.6

 

Mode of heat treatment  1J85

Annealing media

Vacuum with a residual pressure not higher than 0.1Pa, hydrogen with a dew point of not higher than minus 40 ºC.

The heating temperature and rate

1100~1200ºC

Holding time/h

3~6

Cooling rate

With 100 ~ 200 ºC/ h cooled to 500~600 ºC, not less than 400ºC/h cooled to 300ºC

 

Style of supply

Alloys Name

Type

Dimension

 

1J85

Wire

D= 0.1~8mm

 

1J85

Strip

W= 8~390mm

T= 0.3mm

1J85

Foil

W= 10~100mm

T= 0.01~0.1

1J85

Bar

Dia= 8~100mm

L= 50~1000

Send your message to this supplier

*From:
*To:
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now
Contact Supplier