ASTM TM29 DIN Tb1577A General-Purpose Bimetal Strip 5j1580 (5J16)

• Customization: Available
• Standard: GB
• Technique: Cold Drawn
• Model NO.: 5J1580
• Shape: Strip, Roll
• Surface Treatment: Polished
• Size: 0.05mm-3.0mm)T*(1mm-150mm)W
• Condition: Bright,Printed
• Property: Can Replace Kanthal 155
• Brand: Ualloy
• High Expansive Lamination: Ni20mn6
• Low Expensive Lamination: Ni36
• Transport Package: Rolled, Then Packed Into Plywood Pallet or Case
• Trademark: UALLOY
• Origin: Hangzhou, China
• HS Code: 7226999001

Product Description

ASTM TM29 DIN TB1577A General-purpose Bimetal Strip 5J1580(5J16)

Similar marks in different country
 
Chinese mark:5J1580/5J16
German mark:TB1577
EMS:LA1
AUERHAMMER:TB155 / 78
NEOMAX:BL-2
American mark:TM29
 
Description
 
Thermal bimetallic layer is composed of two layers with different linear Solid combination of expansion coefficient of metal composite materials.It holds the higher thermal sensitivity and high resistivity, low temperature stability is good, the welding is more easily and widely used. And it mainly is used for temperature measurement and automatic control equipment in the thermal sensitive element.
 
Component laminations and Chemical content
 
High expansive lamination(Active):Ni20Mn6
Low expensive lamination(Passive):Ni36
 

Layer of alloy components	Chemical content(%)
	Ni	Cr	Fe	Co	Cu	Zn	Mn	Si	C	S	P
									≤
Ni20Mn6	19.0~21.0		Bal.				5.0~7.0	0.15~0.30	0.05	0.02	0.02
Ni36	35.0~37.0		Bal.				≤0.6	≤0.3	0.05	0.02	0.02

                      
Mechanical Properties

Flexivity(F)(at 20-130ºC)	28.5 x 10^-6/ºC
Resistivity(20ºC±5ºC)	0.78±5%Ωmm^2/m
Modulus of elasticity(E)	≥147000 MPa
Linear temperature range	-20~180ºC
Allows the use of temperature range	-70~350ºC
Density	8.1(g/cm3)

 
Description
 
Thermal bimetallic layer is composed of two layers with different linear Solid combination of expansion coefficient of metal composite materials.It holds the higher thermal sensitivity and high resistivity, low temperature stability is good, the welding is more easily and widely used. And it mainly is used for temperature measurement and automatic control equipment in the thermal sensitive element.
 
Component laminations and Chemical content
 
High expansive lamination(Active):Ni20Mn6
Low expensive lamination(Passive):Ni36
 

Layer of alloy components	Chemical content(%)
	Ni	Cr	Fe	Co	Cu	Zn	Mn	Si	C	S	P
									≤
Ni20Mn6	19.0~21.0		Bal.				5.0~7.0	0.15~0.30	0.05	0.02	0.02
Ni36	35.0~37.0		Bal.				≤0.6	≤0.3	0.05	0.02	0.02

                      
Mechanical Properties

Flexivity(F)(at 20-130ºC)	28.5 x 10^-6/ºC
Resistivity(20ºC±5ºC)	0.78±5%Ωmm^2/m
Modulus of elasticity(E)	≥147000 MPa
Linear temperature range	-20~180ºC
Allows the use of temperature range	-70~350ºC
Density	8.1(g/cm3)