Inconel 600 is face-centered cubic lattice structure for use at temperature up to 1425°C (2600°F).The Nickel-Chromium alloy is characterized by good corrosion resistance in the reduction condition,alkaline solution,inorganic acid and good resistance to oxidation at high temperatures.
Chemical Content(%)
| Alloy | % | Ni | Cr | Fe | C | Mn | Si | Cu | P | S |
| Inconel 600 |
Min. | 72 | 14 | 6 | ||||||
| Max. | 17 | 10 | 0.15 | 1 | 0.5 | 0.5 | 0.015 | 0.015 |
| Aolly status | Tensile strength Rm N/mm² |
Yield strength R P 0.2N/mm² |
Elongation A 5 % |
Brinell hardness HB |
Density g/cm³ |
Melting Point °C |
| Annealing treatment |
550 | 240 | 30 | ≤195 | 8.4 | 1370-1425 |
| Annealing treatment |
500 | 180 | 35 | ≤185 | 8.4 | 1370-1425 |
Features
Good corrosion resistance to the reduction, oxidation, Nitric and other media,good stress corrosion cracking resistance,good corrosion resistance of the dry chlorine and chlorine hydride,good mechanical property when below zero, room temperature and high temperature,good anti-creep rupture strength.
Usage
It widely used in following field:
1) Furnace components:heat treatment furnace flask and components.
2) Chemical processing:vinyl chloride monomer production,oxide shaft chloride converted to six fluoride,corrosive alkali metal produce and usage filed,use hlorine produce titanium dioxide,organic or inorganic chlorine produce.
3) Food processing.
5) Petrochemical works production of catalytic regeneration.
Specification
Round Wire:0.03mm~10mm
Flat Wire(Ribbon):thickness 0.1mm~1.0mm,width 0.5mm~5.0mm
Strip:thickness 0.2mm~3.0mm,width 0.5mm~200mm
Other sizes are available upon your request.
Grade Contrast
ASTM(American Society for Testing and Materials):UNS N06600
DIN(Deutsche Industrie Normen):W.Nr.2.4816,NiCrl 5Fe
BS(British Standards):NA14
Products and services
1). Pass: ISO9001 certification, and SO14001cetification;
2). Fine after-sale services;
3). Small order accepted;
4). Fast delivery.
1.Introduction
Inconel Alloy 625 (UNS designation N06625) is a Ni-Cr based superalloy that possesses
high strength properties and resistance to elevated temperatures. It also demonstrates
remarkable protection against corrosion and oxidation. Its ability to withstand high stress
and a wide range of temperatures, both in and out of water, as well as being able to
resist corrosion while being exposed to highly acidic environments makes it a fitting
choice for nuclear and marine applications.
Inconel 625 was developed in the 1960s with the purpose of creating a material that
could be used for steam-line piping. Some modifications were made to its original
composition that have enabled it to be even more creep-resistant and weldable.
Because of this, the uses of Inconel 625 have expanded into a wide range of industries
such as the chemical processing industry, and for marine and nuclear applications
to make pumps and valves and other high pressure equipment.
2.Chemistry
Some chemical properties of Inconel 625 include:
Best price inconel 625 / alloy 625 weld wire
Inconel 625 was designed as a solid solution strengthened material with no significant
microstructure. This holds true at low and high temperatures, but there is a region
(923 to 1148 K) where precipitates form that are detrimental to the creep properties,
and thus the strength, of the alloy. Under any creep conditions (high temperature
with an applied stress), M23C6-type carbides form at the grain boundaries. When
tested at 973 K, γ" precipitates begin forming. These γ" phase precipitates are
ordered A3 B type with a composition of Ni3(Nb, Al, Ti) and a tetragonal crystal structure.
They form a disk-shaped morphology and are coherent with respect to the matrix.
When tested at 998 K, a δ-phase precipitate begins forming which consist of Ni3(Nb, Mo)
in an orthorhombic crystal structure. They form in a needle-like morphology and are
incoherent with the matrix. Both of these precipitates can be completely dissolved back
into the matrix when the sample is heated 1148 K. This leads to the ability to recover creep
properties of the alloy to prolong the materials lifetime.
3.ASTM (American Society for Testing and Materials) for various products made
out of Inconel 625 are as follow:
Pipe Seamless Pipe Welded Tube Seamless Tube Welded Sheet/Plate Bar Forging Fitting Wire
B444 B705 B444 B704 B443 B446 - - -
4.specifications
Specifications and certifications include:
AMS: 5599, 5666
MS: 5837
ASME: SB 443 Gr 1, SB 446 Gr 1
ASTM: B 443 Gr 1, B 446 Gr 1
EN: 2.4856
ISO: 15156-3
NACE: MR0175-3
UNS: N06625
Werkstoff: 2.4856
5.Heat Treatment
Heat Treatment Inconel 625 is usually strengthened by cold work, with annealing at
temperatures between 1,700 and 1,900F as required to remove the effects of cold work.
Although nominally a solid-solution alloy containing intergranular and intragranular
carbide precipitates, Inconel 625 is not responsive to strengthening heat treatments.
Solution heat treating at 2000 to 2200F dissolves almost all of the secondary carbides.
The major effects of short-time annealing of hot-rolled bar of standard composition are
to affect reductions in tensile strength and hardness.Typically, the annealing heat
treatment most utilized for Inconel 625 is at 1800F.