16 Gage C7700 Strip

• Customization: Available
• Product Type: Foil
• Material: Cu,Ni,Zn
• Model NO.: C7701
• Carbon Content: Low Carbon
• Condition: Bright
• Density g/cm3: 8.7
• Electrical Conductivity %Iacs: 5
• Thermal Conductivity W/(M.K): 32
• Modulus of Elasticity Gpa: 125
• Specific Heat J/(G.K): 0.34
• Machinability: Suitable
• Electric Plating Property: Excellent
• Hot DIP Tin Plating Property: Excellent
• Weldability: Good
• Transport Package: in Coil, Carton, Wooden Case
• Specification: RoHS, SGS
• Trademark: Ualloy
• Origin: Zhejiang, China
• HS Code: 74082290
• Production Capacity: 500tons/Year

Product Description

1. Description
 
Copper-Nickel-Zinc alloy, also called nickel silver, German silver, new silver, nickel brass, albata, or electrum, is a copper alloy with nickel and often zinc. Nickel silver is named for its silvery appearance, but it contains no elemental silver unless plated.
 
       Chemical Content(%)
 

Cu	Fe	Mn	Ni	Pb	Zn
54.0~58.0	< 0.25	< 0.5	16.5~19.5	< 0.1	Remainder

 
 Articles,Chemical composition

Articles				Chemical composition
GB	UNS	EN	JIS	Cu%	Ni%	Zn%
BZn18-26	C77000	CuNi18Zn27	C7701	54-58	16.5-19.5	Rem

 
Physical properties,fabrication properties

Physical properties					fabrication properties
density g/cm3	electrical conductivity %IACS	thermal conductivity W/(m.K)	modulus of elasticity GPa	specific heat J/(g.K)	cold-workability	machinability	electric plating property	hot dip tin plating property	weldability	corrosion
8.7	5	32	125	0.34	excellent	suitable	excellent	excellent	good	excellent

 
Mechanical properties

Mechanical properties
State	Hardness HV	Tension test				bending(in rolling direction)rest			bending(transverse to rolling direction)test
		thickness mm	tensile strength MPa	yield strength MPa	elongation%	thickness mm	angles	ID	thickness	angles	ID
1/2H	150-210	0.1-0.7	540-655	≥390	≥8	≤1.6	180°	150% of thickness	≤0.5	180°	300% of thickness
		≥0.71	540-655	≥390	≥11
H	180-240	0.1-0.7	630-735	≥390 ≥500	≥4	≤1.6	180°	200% of thickness	≤0.5	180°	400% of thickness
		≥0.71	630-735	≥500	≥6
EH	210-260	≥0.1	705-805	≥600	-	≤1.6	90°	300% of thickness	≤0.5	90°	600% of thickness
SH	230-270	≥0.1	765-865	≥680	-	-	-	-	-	-	-

 
Typical application
Shields,Liquid crystal oscillators
 
 
 
 
 
       Mechanical Properties
 

Condition	1/2 Hard	Hard
Hardness	150 ~ 210 HV	180 ~ 240 HV
Tensile Strength	540 ~ 655 MPa	630 ~ 735 MPa
Elongation	Min. 8%	Min. 4%

 
 
2. Specification
 

 

Foil:thickness:less than 0.05mm
     width: less than 200mm
 
 
3. Packing detail 
 1). Coil (plastic spool) + compressed ply-wooden case + pallet 
 2). Coil (plastic spool) + carton + pallet  
 5. Products and services
 
4. Products and services
1). Pass: ISO9001 certification, and SO14001cetification;
2). Fine after-sale services;
3). Small order accepted;
4). Fast delivery;